Preparação, caracterização e avaliação de nanocompósitos de PBAT/amido de milho e vermiculita organofilizada

• Ano de defesa: 2015
• Autor(a) principal: Oliveira, Marcelo Ferreira Leão de
• Orientador(a): Leite, Marcia Christina Amorim Moreira
• Banca de defesa: Sousa, Ana Maria Furtado de , Mello, Ivana Lourenço de , Costa, Dilma Alves , Thiré, Rossana Mara da Silva Moreira
• Tipo de documento: Tese
• Tipo de acesso: Acesso aberto
• Idioma: por
• Instituição de defesa: Universidade do Estado do Rio de Janeiro
• Programa de Pós-Graduação: Programa de Pós-Graduação em Química
• Departamento: Centro de Tecnologia e Ciências::Instituto de Química
• País: BR
• Palavras-chave em Português: Polímeros biodegradáveis; vermiculita; nanocompósitos
• Palavras-chave em Inglês: Biodegradable polymers; vermiculite; nanocomposites
• Área do conhecimento CNPq: CNPQ::CIENCIAS EXATAS E DA TERRA::QUIMICA::QUIMICA ORGANICA::POLIMEROS E COLOIDES
• Link de acesso: http://www.bdtd.uerj.br/handle/1/15640

In the last 20-30 years biodegradable polymers have been studied and developed and currently are already commercialized. However, cost, processability and some properties still avoid the penetration of such polymers on the market and the competition with the so-called commodity. There are few authors who are dedicated to developing additives and formulations to overcome these limitations. Thus, this thesis is devoted to the development of Ecobras composites, blend of PBAT and starch manufactured by BASF and commercialized by Corn Products, using as mineral filler a residue of bauxite extraction from Santa Luzia / PB, which consists entirely of vermiculite. The vermiculite was chemically modified with alkyl phosphonium salts to improve compatibility with the polymer matrix, and also to increase the space between aluminosilicate layers. In fact, its modification with hexadecyl tributyl phosphonium bromide promoted the exfoliation of vermiculite making it potentially suitable for obtaining a nanocomposite. The preparation of the composites was performed by the melt intercalation technique. Internal mixing chamber and a twin screw mini-extruder were compared as processing tool, the latter was more effective in dispersing the vermiculite, as revealed by scanning electron microscopy, X-ray diffraction and plate rheometry. The degree of dispersion was also influenced by the amount and chemical structure of the vermiculite. Higher filler levels led to formation of agglomerates, while filler modification led to formation of micro and nanocomposites. There were changes in the thermal properties with increasing temperature values of glass transition, crystallization and melting, although the degree of crystallinity has been retained. Clearly, stiffer materials were obtained, with a higher modulus and low strain capacity. About 58% of weight loss was observed for micro and nanocomposites after 17 weeks of burial in simulated soil for evaluation of biodegradability, very close to pure Ecobras value. Generally, the incorporation of different vermiculite delayed biodegradation in the first weeks, probably due to changes in crystalline structure as suggested by the higher melting temperature values observed during the monitoring of the biodegradation process. However, after seven weeks of the micro and nanocomposites biodegradation profiles approached quite to pure Ecobras. Thus, it was possible in this work obtain a Ecobras nanocomposite with hexadecyl tetrabutyl phosphonium bromide modified vermiculite prepared by melt intercalation technique using common processing tools and with biodegradability close the starting polymer, but more rigid and less deformable