Redução carbotérmica de TiO2 por descarga em cátodo oco

• Ano de defesa: 2011
• Autor(a) principal: Carvalho, Raquel Guilherme de
• Orientador(a): Alves Júnior, Clodomiro
• Tipo de documento: Dissertação
• Tipo de acesso: Acesso aberto
• Idioma: por
• Instituição de defesa: Universidade Federal do Rio Grande do Norte
• Programa de Pós-Graduação: Programa de Pós-Graduação em Engenharia Mecânica
• Departamento: Tecnologia de Materiais; Projetos Mecânicos; Termociências
• País: BR
• Palavras-chave em Português: Dióxido de titânio; Redução carbotérmica; Plasma; DRX e MEV
• Palavras-chave em Inglês: Titanium dioxide; Carbothermal reduction; Plasma; XRD and SEM
• Área do conhecimento CNPq: CNPQ::ENGENHARIAS::ENGENHARIA MECANICA
• Link de acesso: https://repositorio.ufrn.br/jspui/handle/123456789/15673

In this study we used the plasma as a source of energy in the process of carbothermic reduction of rutile ore (TiO2). The rutile and graphite powders were milled for 15 h and placed in a hollow cathode discharge produced by in order to obtain titanium carbonitride directly from the reaction, was verified the influence of processing parameters of plasma temperature and time in the synthesis of TiCN. The reaction was carried out at 600, 700 and 800˚C for 3 to 4 hours in an atmosphere of nitrogen and argon. During all reactions was monitored by plasma technique of optical emission spectroscopy (EEO) to check the active species present in the process of carbothermal reduction of TiO2. The powder obtained after the reactions were characterized by the techniques of X-ray diffraction (XRD) and scanning electron microscopy (SEM). The technique of EEO were detected in all reactions the spectra CO and NO, and these gas-phase resulting from the reduction of TiO2. The results of X-ray diffraction confirmed the reduction, where for all conditions studied there was evidence of early reduction of TiO2 through the emergence of intermediate oxides. In the samples reduced at 600 and 700˚C, there was only the phase Ti6O11, those reduced to 800˚C appeared Ti5O9 phases, and Ti6O11 Ti7O13, confirming that the carbothermal reduction in plasma, a reduction of the ore rutile (TiO2) in a series of intermediate titanium oxide (TinO2n-1) where n varies between 5 and 10