Desenvolvimento de suportes vítreos e vitrocerâmicos baseados no sistema Li2O-BaO-SiO2 mofificados pelos óxidos Nb2O5, TiO2, V2O5 e ZrO2, para microextração em fase sólida (SPME-CG)

• Ano de defesa: 2012
• Autor(a) principal: Percio, Maycon Fernando
• Orientador(a): Campos, Elvio Antonio de
• Banca de defesa: Borba, Carlos Eduardo , Tanamati, Ailey Aparecida Coelho
• Tipo de documento: Dissertação
• Tipo de acesso: Acesso aberto
• Idioma: por
• Instituição de defesa: Universidade Estadual do Oeste do Paraná; Toledo
• Programa de Pós-Graduação: Programa de Pós-Graduação em Engenharia Química
• Departamento: Desenvolvimento de Processos
• País: BR
• Palavras-chave em Português: Fibra de vidro; Vitrocerâmico; Microextração em fase sólida; HS-SPME-CG; Cromatografia gasosa; Materiais vitrocerâmicos; Cromatrografia à gás
• Palavras-chave em Inglês: Glass fiber; Glass-ceramics; Solid phase micro extraction; HS-SPME-GC; Ceramics
• Área do conhecimento CNPq: ENGENHARIAS::ENGENHARIA QUÍMICA::PROCESSOS INDUSTRIAIS DE ENGENHARIA QUÍMICA
• Link de acesso: http://tede.unioeste.br:8080/tede/handle/tede/1911

In the present work a vitreous composition based on combination of the oxides BaO-SiO2-Li2O modified by adding of oxides Nb2O5, TiO2, V2O5 and ZrO2 as nucleating agent was evaluated and used in the manufacture of glass and glass-ceramic fibers for use in SPME-CG. The stability of the resulting glasses was accompained by X-ray diffraction (XRD) and differential thermal analysis (DTA). The stability parameters of Weinberg (KW), Hubrÿ (KH), Lu e Liu (KLL), Du and Huang (KDU) and Saad and Poulain (KSP) were obtained by DTA data. By KSP was observed that stability of glassy phases follows the descending order: Composition 5 (ZrO2) > Composition 2 (Nb2O5) > Composition 1 (without nucleant) > Composition 4 (V2O5) > Composition 3 (TiO2). Through these data it was possible to determine the apparent activation energies of the crystallization process by the crystallization peaks of the DTA curves, whereby the decreasing order was obtained: Composition 5 (ZrO2)> Composition 4 (V2O5) > Composition 2 (Nb2O5) > Composition 3 (TiO2) > Composition 1 (without nucleant). It was found, through the Avrami index, a surface crystallization mechanism of the compositions that leads to a correspondent transition to the glass ceramic. From DRX data obtained after thermal treatment at varying time, the TTT diagrams (Time, Temperature and Transformation) of the compositions were constructed, which delimited the conditions for preparation of glass ceramic fibers. The XRD analysis indicated that the main crystalline phases formed after heat treatments are rhombic Li2SiO3 Li2Si2O5. The fibers obtained were further tested in chromatographic analysis by HS-SPME-GC of the methanol in aqueous solution at concentrations of 10 and 100 mgL-1 with satisfactory results.