Estudo de microscopia eletrônica de transmissão in situ de nanoestrutura de óxidos mistos em altas temperaturas

• Ano de defesa: 2018
• Autor(a) principal: Maya Johnson, Santiago
• Orientador(a): Leite, Edson Roberto
• Tipo de documento: Tese
• Tipo de acesso: Acesso aberto
• Idioma: eng
• Instituição de defesa: Universidade Federal de São Carlos; Câmpus São Carlos
• Programa de Pós-Graduação: Programa de Pós-Graduação em Ciência e Engenharia de Materiais - PPGCEM
• Palavras-chave em Português: Microscopia Eletrônica de Transmissão de Alta Resolução (HRTEM); Microscopia Eletrônica de Transmissão in situ; Nanopartículas de óxidos metálicos; Síntese de nanopartículas; Fixação orientada
• Palavras-chave em Inglês: High-Resolution Transmission Electron Microscopy (HRTEM); In situ transmission electron microscopy; Metal oxide nanoparticles; Nanoparticle synthesis; Oriented attachment
• Área do conhecimento CNPq: ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA::MATERIAIS NAO METALICOS; ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA; ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA::MATERIAIS NAO METALICOS::CERAMICOS; CIENCIAS EXATAS E DA TERRA::QUIMICA::QUIMICA INORGANICA::NAO-METAIS E SEUS COMPOSTOS
• Link de acesso: https://repositorio.ufscar.br/handle/20.500.14289/10668

This work addresses the characterization of the high temperature reactions between different nanoparticles oxides, CeO2-ZrO2 and CeO2-SnO2, by the direct observation of the phenomenon by in situ Transmission Electron Microscopy (TEM). The nanoparticles were synthesized via three different synthesis methods, hydrothermal, solvothermal, and solvent-control. The changes in the size and morphology of the nanoparticles, the interactions that lead to processes of sintering / densification, and the phase transformations that occur during the experiments were documented. Also, a detailed study of the influence of the electron beam current density on the sample, and its synergism with the temperature during the in situ experiments was performed. The interactions between the oxide metal nanoparticles and the films of the TEM grids showed a great influence during the in situ tests at high temperature. For the experimental setups tested in this work, the main mechanism of interaction between the nanoparticles was oriented attachment.