Sinterização de Ce1-XEuXO2-(X/2) para aplicação como eletrólito sólido em células a combustível de temperaturas intermediárias

• Ano de defesa: 2010
• Autor(a) principal: Souza, Ana Karolina Bezerra de
• Tipo de documento: Dissertação
• Tipo de acesso: Acesso aberto
• Idioma: por
• Instituição de defesa: Universidade Federal do Rio Grande do Norte; BR; UFRN; Programa de Pós-Graduação em Ciência e Engenharia de Materiais; Processamento de Materiais a partir do Pó; Polímeros e Compósitos; Processamento de Materiais a part
• Palavras-chave em Português: Célula a combustível; Céria-európia; Eletrólito; Sinterização em duas etapas; SOFC; Ceria doped with europeia; Electrolyte; Two step sintering; CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA
• Link de acesso: https://repositorio.ufrn.br/jspui/handle/123456789/12708

Given the environmental concern over global warming that occurs mainly by emission of CO2 from the combustion of petroleum, coal and natural gas research focused on alternative and clean energy generation has been intensified. Among these, the highlight the solid oxide fuel cell intermediate temperature (IT-SOFC). For application as electrolyte of the devices doped based CeO2 with rare earth ions (TR+ 3) have been quite promising because they have good ionic conductivity and operate at relatively low temperatures (500-800 ° C). In this work, studied the Ce1-xEuxO2-δ (x = 0,1, 0,2 and 0,3), solid solutions synthesized by the polymeric precursor method to be used as solid electrolyte. It was also studied the processing steps of these powders (milling, compaction and two step sintering) in order to obtain dense sintered pellets with reduced grain size and homogeneous microstructure. For this, the powders were characterized by thermal analysis, X-ray diffraction, particle size distribution and scanning electrons microscopy, since the sintered samples were characterized by dilatometry, scanning electrons microscopy, density and grain size measurements. By x-ray diffraction, it was verified the formation of the solid solution for all compositions. Crystallites in the nanometric scale were found for both sintering routes but the two step sintering presented significant reduction in the average grain size