Influência da absorção de umidade no comportamento mecânico nos compósitos poliméricos híbridos Kevlar/vidro quando imerso em água do mar e petróleo

• Ano de defesa: 2015
• Autor(a) principal: Cunha, Ricardo Alex Dantas da
• Tipo de documento: Dissertação
• Tipo de acesso: Acesso aberto
• Idioma: por
• Instituição de defesa: Universidade Federal do Rio Grande do Norte; Brasil; UFRN; PROGRAMA DE PÓS-GRADUAÇÃO EM ENGENHARIA MECÂNICA
• Palavras-chave em Português: Fibra de Vidro-E; Fibra de Kevlar; Absorção de umidade; Propriedades mecânicas; Água do mar; Petróleo; CNPQ::ENGENHARIAS::ENGENHARIA MECANICA
• Link de acesso: https://repositorio.ufrn.br/jspui/handle/123456789/20605

The polymer matrix composite materials are being used on a large scale in the most different industrial fields such as aerospace, automotive, oil, among others, since the industrial perspectives is currently working with materials which have a good mechanical performance at high service life and cost / benefit. Thus, the determination of the mechanical properties is indispensable for the characterization of waste resulting in greater expansion of this type of material. Thus, this work will be obtained three plates laminated with tereftálica polymeric matrix reinforced by a bidirectional woven E-glass and kevlar both industrially made, where the plates are manufactured by manual lamination process (hand lay-up), all laminates have five enhancement layers, the first hybrid laminate will consist of bidirectional woven E-glass fiber, kevlar fiber interspersed with layers, is formed by the second bidirectional woven kevlar fiber at the ends of the laminate (two layers), and in the center the glass fiber fabric (three layers), the third plate is composed of only the bidirectional woven E-glass fiber. Then were prepared specimens (CP) by standard, to determine the mechanical properties of tensile and bending in three points. After fabrication of the specimens, they were immersed in oil and seawater. After that, there was a comparison of the mechanical properties for the test condition in the dry state. Showing that there was a considerable increase in the properties studied because the effect of hybridization in laminates.