Melhorando o desempenho de discos de titânio embalados por meio do tratamento com plasma atmosférico frio

Detalhes bibliográficos
Ano de defesa: 2025
Autor(a) principal: Martins, Gabriel de Moura
Orientador(a): Alves Júnior, Clodomiro
Banca de defesa: Não Informado pela instituição
Tipo de documento: Dissertação
Tipo de acesso: Acesso aberto
Idioma: por
Instituição de defesa: Universidade Federal do Rio Grande do Norte
Programa de Pós-Graduação: PROGRAMA DE PÓS-GRADUAÇÃO EM CIÊNCIAS DA SAÚDE
Departamento: Não Informado pela instituição
País: BR
Palavras-chave em Português:
Titanio (Ti)
Hemocompatibilidade
Implantes
Área do conhecimento CNPq:
CIENCIAS DA SAUDE
Link de acesso: https://repositorio.ufrn.br/handle/123456789/65390
Resumo: Although titanium (Ti)-based bone implants are already clinically established, ongoing research is being conducted to advance the fields of osseointegration and bacterial resistance, seeking further improvements in these areas. In this study, we present an innovative method for the treatment of Ti surfaces in hermetically sealed packaging. Ti discs in surgical-grade packaging were treated with cold atmospheric plasma (CAP). The surfaces were characterized in terms of wettability, crystal structure, and chemical composition. Hemocompatibility analyses were performed using sodium citrate-diluted blood (1:9 ratio) exposed to Ti disks for 30 minutes in a CO2 incubator at 37 °C. Subsequent evaluations included complete blood count (leukocytes, lymphocytes, neutrophils, and erythrocytes), prothrombin time (PT), activated partial thromboplastin time (APTT), and platelet adhesion. Microbiological analyses were conducted using Pseudomonas aeruginosa (ATCC 27853) incubated for 4 hours at 37 °C. CAP treatment reduced the contact angle without altering the crystalline structure. No statistical differences were observed in blood count parameters. Plasma-treated samples exhibited significantly lower PT and APTT values compared to the control group. Platelet adhesion assessments revealed that CAP-treated surfaces showed increased platelet activation, platelet density, and thrombus formation compared to untreated samples. Additionally, treated surfaces demonstrated reduced bacterial colony formation relative to untreated surfaces. Thus, CAP emerges as a promising strategy for optimizing Ti-based bone implants in clinical settings.
id UFRN_37e24140075bb510b520451d9fa50f36
oai_identifier_str oai:repositorio.ufrn.br:123456789/65390
network_acronym_str UFRN
network_name_str Repositório Institucional da UFRN
repository_id_str
spelling Martins, Gabriel de Mourahttps://orcid.org/0000-0001-6489-4187http://lattes.cnpq.br/6746106913768611http://lattes.cnpq.br/7441669258580942Cruz, Nilson Cristinohttps://orcid.org/0000-0002-0354-3890http://lattes.cnpq.br/7157327220048138Araújo Júnior, Raimundo Fernandes dehttps://orcid.org/0000-0003-2349-2354http://lattes.cnpq.br/1903940945895093Alves Júnior, Clodomiro2025-09-01T23:15:58Z2025-09-01T23:15:58Z2025-05-05MARTINS, Gabriel de Moura. Melhorando o desempenho de discos de titânio embalados por meio do tratamento com plasma atmosférico frio. Orientador: Dr. Clodomiro Alves Júnior. 2025. 49f. Dissertação (Mestrado em Ciências da Saúde) - Centro de Ciências da Saúde, Universidade Federal do Rio Grande do Norte, Natal, 2025.https://repositorio.ufrn.br/handle/123456789/6539023001011031P8Although titanium (Ti)-based bone implants are already clinically established, ongoing research is being conducted to advance the fields of osseointegration and bacterial resistance, seeking further improvements in these areas. In this study, we present an innovative method for the treatment of Ti surfaces in hermetically sealed packaging. Ti discs in surgical-grade packaging were treated with cold atmospheric plasma (CAP). The surfaces were characterized in terms of wettability, crystal structure, and chemical composition. Hemocompatibility analyses were performed using sodium citrate-diluted blood (1:9 ratio) exposed to Ti disks for 30 minutes in a CO2 incubator at 37 °C. Subsequent evaluations included complete blood count (leukocytes, lymphocytes, neutrophils, and erythrocytes), prothrombin time (PT), activated partial thromboplastin time (APTT), and platelet adhesion. Microbiological analyses were conducted using Pseudomonas aeruginosa (ATCC 27853) incubated for 4 hours at 37 °C. CAP treatment reduced the contact angle without altering the crystalline structure. No statistical differences were observed in blood count parameters. Plasma-treated samples exhibited significantly lower PT and APTT values compared to the control group. Platelet adhesion assessments revealed that CAP-treated surfaces showed increased platelet activation, platelet density, and thrombus formation compared to untreated samples. Additionally, treated surfaces demonstrated reduced bacterial colony formation relative to untreated surfaces. Thus, CAP emerges as a promising strategy for optimizing Ti-based bone implants in clinical settings.Embora os implantes ósseos a base de titânio (Ti) já esteja clinicamente estabelecida, pesquisas contínuas estão sendo realizadas para avançar nos campos da osteointegração e resistência bacteriana, buscando melhorias adicionais nessas áreas. Neste estudo, apresentamos um método inovador para tratar superfícies de Ti dentro de embalagens hermeticamente fechadas. Discos de Ti em embalagens cirúrgicas, foram submetidos a tratamento usando plasma atmosférico a frio (CAP). As superfícies foram caracterizadas em termos de molhabilidade, estrutura cristalina e composição química. Análises de hemocompatibilidade foram realizadas utilizando sangue diluído em citrato de sódio (1:9) exposto a discos de Ti por 30 minutos dentro de um incubador de CO2 a 37 °C. Posteriormente, foram realizadas avaliações como hemograma (leucócitos, linfócitos, neutrófilos e hemácias), tempo de protrombina (PT), tempo de tromboplastina parcial ativada (APTT) e adesão de plaquetas. Análises microbiológicas também foram realizadas utilizando Pseudomonas aeruginosa (ATCC 27853) por 4 horas a 37 °C. O tratamento com CAP resultou em uma redução no ângulo de contato sem causar alterações na estrutura cristalina. Não foram observadas diferenças estatísticas no hemograma. As amostras tratadas com plasma apresentaram valores de PT e APTT mais baixos em comparação com o grupo controle com diferenças significativas observadas. As avaliações de adesão plaquetária mostraram que as superfícies tratadas com CAP teve aumento na ativação das plaquetas, densidade de plaquetas e formação de trombos quando comparadas com as amostras não tratadas. Além disso, as superfícies tratadas demonstraram menor formação de colônias bacterianas em comparação com outras superfícies. Dessa maneira, o CAP demonstra ser uma estratégia promissora para otimizar implantes ósseos de Ti em ambientes clínicos.Universidade Federal do Rio Grande do NortePROGRAMA DE PÓS-GRADUAÇÃO EM CIÊNCIAS DA SAÚDEUFRNBRCIENCIAS DA SAUDETitanio (Ti)HemocompatibilidadeImplantesMelhorando o desempenho de discos de titânio embalados por meio do tratamento com plasma atmosférico frioinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisinfo:eu-repo/semantics/openAccessporreponame:Repositório Institucional da UFRNinstname:Universidade Federal do Rio Grande do Norte (UFRN)instacron:UFRNORIGINALMelhorandodesempenhodiscos_Martins_2025.pdfapplication/pdf7597380https://repositorio.ufrn.br/bitstreams/ed6db8c6-282d-4031-8775-e2d3dc8862e0/download21345e27dd63b89771535f7df61a62baMD51trueAnonymousREADLICENSElicense.txtWritten by org.dspace.content.LicenseUtilstext/plain; charset=utf-81569https://repositorio.ufrn.br/bitstreams/7b2a2c23-cfd4-45ec-903a-3d9fc0a3bb2f/download6e6f57145bc87daf99079f06b081ff9fMD52falseAnonymousREAD123456789/653902026-08-26T14:14:47.961357Zopen.accessoai:repositorio.ufrn.br:123456789/65390https://repositorio.ufrn.brRepositório InstitucionalPUBhttp://repositorio.ufrn.br/oai/repositorio@bczm.ufrn.bropendoar:2026-08-26T14:14:47Repositório Institucional da UFRN - Universidade Federal do Rio Grande do Norte (UFRN)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
dc.title.none.fl_str_mv Melhorando o desempenho de discos de titânio embalados por meio do tratamento com plasma atmosférico frio
title Melhorando o desempenho de discos de titânio embalados por meio do tratamento com plasma atmosférico frio
spellingShingle Melhorando o desempenho de discos de titânio embalados por meio do tratamento com plasma atmosférico frio
Martins, Gabriel de Moura
CIENCIAS DA SAUDE
Titanio (Ti)
Hemocompatibilidade
Implantes
title_short Melhorando o desempenho de discos de titânio embalados por meio do tratamento com plasma atmosférico frio
title_full Melhorando o desempenho de discos de titânio embalados por meio do tratamento com plasma atmosférico frio
title_fullStr Melhorando o desempenho de discos de titânio embalados por meio do tratamento com plasma atmosférico frio
title_full_unstemmed Melhorando o desempenho de discos de titânio embalados por meio do tratamento com plasma atmosférico frio
title_sort Melhorando o desempenho de discos de titânio embalados por meio do tratamento com plasma atmosférico frio
author Martins, Gabriel de Moura
author_facet Martins, Gabriel de Moura
author_role author
dc.contributor.authorID.none.fl_str_mv https://orcid.org/0000-0001-6489-4187
dc.contributor.authorLattes.none.fl_str_mv http://lattes.cnpq.br/6746106913768611
dc.contributor.advisorLattes.none.fl_str_mv http://lattes.cnpq.br/7441669258580942
dc.contributor.referees1.pt_BR.fl_str_mv Cruz, Nilson Cristino
dc.contributor.referees1ID.none.fl_str_mv https://orcid.org/0000-0002-0354-3890
dc.contributor.referees1Lattes.none.fl_str_mv http://lattes.cnpq.br/7157327220048138
dc.contributor.referees2.none.fl_str_mv Araújo Júnior, Raimundo Fernandes de
dc.contributor.referees2ID.none.fl_str_mv https://orcid.org/0000-0003-2349-2354
dc.contributor.referees2Lattes.none.fl_str_mv http://lattes.cnpq.br/1903940945895093
dc.contributor.author.fl_str_mv Martins, Gabriel de Moura
dc.contributor.advisor1.fl_str_mv Alves Júnior, Clodomiro
contributor_str_mv Alves Júnior, Clodomiro
dc.subject.cnpq.fl_str_mv CIENCIAS DA SAUDE
topic CIENCIAS DA SAUDE
Titanio (Ti)
Hemocompatibilidade
Implantes
dc.subject.por.fl_str_mv Titanio (Ti)
Hemocompatibilidade
Implantes
description Although titanium (Ti)-based bone implants are already clinically established, ongoing research is being conducted to advance the fields of osseointegration and bacterial resistance, seeking further improvements in these areas. In this study, we present an innovative method for the treatment of Ti surfaces in hermetically sealed packaging. Ti discs in surgical-grade packaging were treated with cold atmospheric plasma (CAP). The surfaces were characterized in terms of wettability, crystal structure, and chemical composition. Hemocompatibility analyses were performed using sodium citrate-diluted blood (1:9 ratio) exposed to Ti disks for 30 minutes in a CO2 incubator at 37 °C. Subsequent evaluations included complete blood count (leukocytes, lymphocytes, neutrophils, and erythrocytes), prothrombin time (PT), activated partial thromboplastin time (APTT), and platelet adhesion. Microbiological analyses were conducted using Pseudomonas aeruginosa (ATCC 27853) incubated for 4 hours at 37 °C. CAP treatment reduced the contact angle without altering the crystalline structure. No statistical differences were observed in blood count parameters. Plasma-treated samples exhibited significantly lower PT and APTT values compared to the control group. Platelet adhesion assessments revealed that CAP-treated surfaces showed increased platelet activation, platelet density, and thrombus formation compared to untreated samples. Additionally, treated surfaces demonstrated reduced bacterial colony formation relative to untreated surfaces. Thus, CAP emerges as a promising strategy for optimizing Ti-based bone implants in clinical settings.
publishDate 2025
dc.date.accessioned.fl_str_mv 2025-09-01T23:15:58Z
dc.date.available.fl_str_mv 2025-09-01T23:15:58Z
dc.date.issued.fl_str_mv 2025-05-05
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.citation.fl_str_mv MARTINS, Gabriel de Moura. Melhorando o desempenho de discos de titânio embalados por meio do tratamento com plasma atmosférico frio. Orientador: Dr. Clodomiro Alves Júnior. 2025. 49f. Dissertação (Mestrado em Ciências da Saúde) - Centro de Ciências da Saúde, Universidade Federal do Rio Grande do Norte, Natal, 2025.
dc.identifier.uri.fl_str_mv https://repositorio.ufrn.br/handle/123456789/65390
dc.identifier.capesdegreeprogramcode.pt_BR.fl_str_mv 23001011031P8
identifier_str_mv MARTINS, Gabriel de Moura. Melhorando o desempenho de discos de titânio embalados por meio do tratamento com plasma atmosférico frio. Orientador: Dr. Clodomiro Alves Júnior. 2025. 49f. Dissertação (Mestrado em Ciências da Saúde) - Centro de Ciências da Saúde, Universidade Federal do Rio Grande do Norte, Natal, 2025.
23001011031P8
url https://repositorio.ufrn.br/handle/123456789/65390
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.publisher.none.fl_str_mv Universidade Federal do Rio Grande do Norte
dc.publisher.program.fl_str_mv PROGRAMA DE PÓS-GRADUAÇÃO EM CIÊNCIAS DA SAÚDE
dc.publisher.initials.fl_str_mv UFRN
dc.publisher.country.fl_str_mv BR
publisher.none.fl_str_mv Universidade Federal do Rio Grande do Norte
dc.source.none.fl_str_mv reponame:Repositório Institucional da UFRN
instname:Universidade Federal do Rio Grande do Norte (UFRN)
instacron:UFRN
instname_str Universidade Federal do Rio Grande do Norte (UFRN)
instacron_str UFRN
institution UFRN
reponame_str Repositório Institucional da UFRN
collection Repositório Institucional da UFRN
bitstream.url.fl_str_mv https://repositorio.ufrn.br/bitstreams/ed6db8c6-282d-4031-8775-e2d3dc8862e0/download
https://repositorio.ufrn.br/bitstreams/7b2a2c23-cfd4-45ec-903a-3d9fc0a3bb2f/download
bitstream.checksum.fl_str_mv 21345e27dd63b89771535f7df61a62ba
6e6f57145bc87daf99079f06b081ff9f
bitstream.checksumAlgorithm.fl_str_mv MD5
MD5
repository.name.fl_str_mv Repositório Institucional da UFRN - Universidade Federal do Rio Grande do Norte (UFRN)
repository.mail.fl_str_mv repositorio@bczm.ufrn.br
_version_ 1876429199978266624

Registros relacionados