Caracterização dos eletrocatalisadores LaMnO3, LaFeO3, LaFe0,2Mn0,8O3 E La0,5Fe0,5MnO3 preparados por autocombustão assistida por microondas para cátodos de células a combustível do tipo SOFC

• Ano de defesa: 2013
• Autor(a) principal: Costa, Romário Cezar Pereira da
• Orientador(a): Huitle, Carlos Alberto Martinez
• Tipo de documento: Dissertação
• Tipo de acesso: Acesso aberto
• Idioma: por
• Instituição de defesa: Universidade Federal do Rio Grande do Norte
• Programa de Pós-Graduação: Programa de Pós-Graduação em Química
• Departamento: Físico-Química; Química
• País: BR
• Palavras-chave em Português: Células a combustível. Microondas. Perovskita. Eletrocatalisador
• Palavras-chave em Inglês: Fuel cells. Microwave. Perovskite. Electrocatalyst
• Área do conhecimento CNPq: CNPQ::CIENCIAS EXATAS E DA TERRA::QUIMICA
• Link de acesso: https://repositorio.ufrn.br/jspui/handle/123456789/17744

Materials consisting of perovskite-type oxides (ABO3) have been developed in this work for applications in fuel cell cathodes of solid oxide type (SOFC). These ceramic materials are widely studied for this type of application because they have excellent electrical properties, conductivity and electrocatalytic. The oxides LaMnO3, LaFeO3, LaFe0.2Mn0.8O3 e La0.5Fe0.5MnO3 were synthesized by the method of microwave assisted combustion and after sintering at 800°C in order to obtain the desired phases. The powders were characterized by thermogravimetry (TG), X-ray diffraction (XRD), X-ray fluorescence (XRF), scanning electron microscopy (SEM) and voltammetric analysis (cyclic voltammetry and polarization curves). The results obtained by XRF technique showed that the microwave synthesis method was effective in obtaining doping oxides with values near stoichiometric. In general, powders were obtained with particle size less than 0.5 μm, having a porous structure and uniform particle size distribution. The particles showed spherical form, irregular and crowded of varying sizes, according to the analysis of SEM. The behavior of the oxides opposite the thermal stability was monitored by thermogravimetric curves (TG), which showed low weight loss values for all samples, especially those of manganese had its structure. By means of Xray diffraction of the samples sintered at 800°C was possible to observe the formation of powders having high levels of crystallinity. Furthermore, undesirable phases such as La2O3 and MnOx were not identified in the diffractograms. These phases block the transport of oxygen ions in the electrode/electrolyte interface, affecting the electrochemical activity of the system. The voltammetric analysis of the electrocatalysts LF-800, LM-800, LF2M8-800 e L5F5M-800 revealed that these materials are excellent electrical conductors, because it increased the passage of electrical current of the working electrode significantly. Best performance for the oxygen reduction reaction was observed with iron-rich structures, considering that the materials obtained have characteristics suitable for use in fuel cell cathodes of solid oxide type