Síntese e caracterização estrutural, magnética e térmica da hidroxiapatita dopada com ferro

• Ano de defesa: 2014
• Autor(a) principal: Santos, Wellington Cantanhede dos
• Tipo de documento: Dissertação
• Tipo de acesso: Acesso aberto
• Idioma: por
• Instituição de defesa: Universidade Federal do Rio Grande do Norte; Brasil; UFRN; PROGRAMA DE PÓS-GRADUAÇÃO EM FÍSICA
• Palavras-chave em Português: Nanopartículas; hidroxiapatita; moagem de alta energia; raios X; magnetização; hipertermia magnética.; CNPQ::CIENCIAS EXATAS E DA TERRA::FISICA
• Link de acesso: https://repositorio.ufrn.br/jspui/handle/123456789/19377

In this work, composites were prepared using high energy mechanical milling from the precursors hydroxyapatite - HAp (Ca10(PO4)6(OH)2) and metallic iron ( -Fe ). The main goal here is to study composites in order to employ them in magnetic hyperthermia for cancer therapy. The produced samples were characterized by X-ray di raction (XRD), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), magnetization curves as a function of applied eld (MxH), and nally measurements of magnetic hyperthermia. The XRD patterns of the milled samples HAp/Fe revealed only the presence of precursor materials. The SEM showed clusters with irregular shapes. The magnetization curves indicated typical cases of weak ferromagnetic behavior. For samples submitted to grinding and annealing, the identi ed phases were: HAp (Ca10(PO4)6(OH)2), hematite (Fe2O3) and Calcium Iron Phosphate (Ca9Fe(PO4)7). Analyzing the results of MxH, there was a reduction of the saturation magnetization, given that the Fe was incorporated into HAp. Hysteresis curves obtained at 300 K are characteristics of samples possessing over a phase. At 77 K, the behavior of the hysteresis curve is in uenced by the presence of hematite, which is antiferromagnetic. Already at T = 4.2 K, it is observed a weak ferromagnetic behavior. Furthermore, there is the e ect of exchange bias. Regarding the magnetic hyperthermia, the results of temperature measurements as a function of the alternating eld are promising for applications in magnetic hyperthermia and other biomedical applications.