Ativação alcali-sílica por aplicação de micro-ondas e passivação de agregado reativo por tratamento com nitrato de lítio

• Ano de defesa: 2020
• Autor(a) principal: Doria, Mariana Rezende
• Orientador(a): Barreto, Ledjane Silva
• Tipo de documento: Tese
• Tipo de acesso: Acesso aberto
• Idioma: por
• Programa de Pós-Graduação: Pós-Graduação em Ciência e Engenharia de Materiais
• Palavras-chave em Português: Engenharia de materiais; Microondas; Lítio; Reações químicas
• Palavras-chave em Inglês: Lithium; Microwave; Silica reaction
• Área do conhecimento CNPq: ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA
• Link de acesso: https://ri.ufs.br/jspui/handle/riufs/14759

The alkali-silica reaction (ASR), is is a type of akali-silica reaction, developed in the presence of reactive mineral aggregates, is responsible for numerous cases of cracking and even collapse of concrete structures. This work presents a contribution to the development of a chemical method for the activation of the alkali-silica reactivity of an aggregate in its commercial granulometry, in a short time, through the application of microwaves and verification of lithium nitrate addition influence to mitigate the reaction. A proven reactive granite aggregate was used at different microwave application times with a fixed power of 700 W, in neutral and basic media. Results on the aggregate reactivity were obtained in 5 minutes of microwave application, statistically equivalent to tests with 30 days immersion. It was observed that the most affected phases during the process are non-crystalline silica, and a gel-like phase similar to the alkali-silica reaction product was also obtained at the end of the tests. In addition, a pre-treatment of the aggregate was performed with 0.5 to 2% lithium nitrate additions, with and without microwaves, in neutral and basic media. It was observed that additions of at least 0.5% significantly inhibit the silica dissolution, and that there is the formation of a non-crystalline coating of lithium silicate, which prevents the dissolution of silica and, consequently, the continuation of the RAS mechanism.