Determinação da estabilidade de fases à 1300oC do sistema Al2O3-Y2O3-Ta2O5

• Ano de defesa: 2023
• Autor(a) principal: Oliveira, Juliana Pereira De
• Orientador(a): Ramos, Alfeu Saraiva
• Banca de defesa: Santos, Claudinei Dos, Freitas, Bruno Xavier De
• Tipo de documento: Dissertação
• Tipo de acesso: Acesso aberto
• Idioma: por
• Instituição de defesa: Universidade Federal de Alfenas
• Programa de Pós-Graduação: Programa de Pós-Graduação em Ciência e Engenharia de Materiais
• Departamento: Instituto de Ciência e Tecnologia
• País: Brasil
• Palavras-chave em Português: Diagrama de Fases.; Tratamento Térmico.; Óxido de Alumínio.; Óxido de Ítrio.; Pentóxido de Tântalo.
• Área do conhecimento CNPq: ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA
• Link de acesso: https://repositorio.unifal-mg.edu.br/handle/123456789/2348

Ceramics of pseudo-ternary Al2O3-Y2O3-Ta2O5 system have potential for applications in engineering areas due to the mechanical properties in compression and fracture toughness of Al2O3-Y2O3 ceramics and others Al2O3-Ta2O5 ceramics related to catalytic processes. However, no information on the phase stability of the Al2O3-Y2O3-Ta2O5 system was found in the literature. Thus, the present research aims to determine the phase stability at 1300ºC of this pseudo-ternary system. Information from the corresponding pseudo-binary systems will be used for an initial proposition of possible biphasic and/or three-phase regions. Based on this information, different chemical compositions, in mol-%, were considered. After weighing, the mixtures of Al2O3, Y2O3 and Ta2O5 powders were homogenized in a ball mill for 10 min, using a WC vial (80mL) and alumina balls (10mm in diameter), to minimize their contamination. In sequence, the cylinder samples with 10 mm diameter were prepared by axial pressing of 187 MPa. The green compacts of Al2O3-Y2O3-Ta2O5 ceramics were heat-treated at 1300ºC for 72 h and 222 h, aiming to obtain equilibrium microstructures. Samples of heat-treated Al2O3-Y2O3-Ta2O5 ceramics were characterized by means of X-ray diffractometry, scanning electron microscopy and energy dispersive spectrometry techniques. The results have confirmed the existence of three-phase Y2O3+Y4Al2O9+Y3TaO7 and YTa7O19+AlTaO4+Ta2O5 regions from the 11.11Al2O3 – 8.33Ta2O5-80.56Y2O3 and 16.67Al2O3-78.57Ta2O5-4.76Y2O3 (mol-%), respectively.